China Thermoplastic Polyimide Resin
- Min.Order: 100 Kilogram
- Payment Terms: L/C,T/T
- Product Details
Keywords
- Resin
- Thermoplastic Polyimide Resin
- SolverPI-Resin 6002
Quick Details
- ProName: China Thermoplastic Polyimide Resin
- Appearance: faint yellow powder.
- Application: The applied range of SolverPI-Resin 60...
- DeliveryTime: 30days
- PackAge: 5kg/bag,25kg/drum
- Port: shanghai
- ProductionCapacity: 1000 Kilogram/Day
- Purity: .
- Storage: powder,granule,proximate matter
- LimitNum: 100 Kilogram
Superiority
Product Name: Thermoplastic Polyimide Resin
Item No.: SolverPI-Resin 6002
SolverPI-Resin 6002 is produced by SOLVER POLYIMIDE which has good machinability. It can be mould pressing,injection molding, extrusion molding.The themoplastic polymide can be reprocessed and mixed with graphite,carbon black,fiberglass,ceramic powder,carbon fiber,aramid fiber,metal powder,molybdenum disulfide,invisible material and so on to change its characters,producing the bearing,valve,seal part,pipe panel all kinds of mechine parts,and invisible marterial.
The characteristic of SolverPI-Resin 6002
·High heat resistence.Can be long-uesd in temperature＞300℃.
·Excellent lubricity.Low COFand low frictional loss.
·High insulation,low Coefficient of Linear Thermal Expansion,deformation resistence,acid and alkalicresistence,salt tolerance,non-corroding.
·Radiation resistant.N appearance change under the 200kGyirradiatiin of ray.
Extremely low hydroscopicity.Resistence to water wapor,no hydrolysis.
·Low thermalconductivity.Good thermal insulation properties,low calorific value when it runs up.
·The low dielectyic constant.High impedance,no reflection to radar,good base material of invisible material.
·Fire retardant level FV-level 0.
The applied range of SolverPI-Resin 6002
With the superior property,the ZTS-PI-I can be used in petrochemical industry,mining machinery,precision machinery,automobile industry,micro-electronic device,medical apparatus and instruments,aviation,aerospace,guided missile,naval vessels and so on.
In high speed and high pressure applications,parts with low COF and abrasion resistence.
Parts with good creep resistence and low plastic deformation.
Parts with good self-lubricating and good lubrication performance.
Parts with high bending、stretching、striking properties
Parts with high fire retardant level(no metal)
Parts with wave-transparent、microwave absorpting、invisible properties.
The permance index of SolverPI-Resin 6002
|
Terms of detection |
Guideposts |
Test standard and methods |
|
Density（g/cm³） |
1.28-1.32 |
GB/T1033.1-2008 |
|
Bending strength(MPa)(23℃±2℃) |
＞850 |
GB9341-2008 |
|
Flexural modulus(MPa)(23℃±2℃) |
＞25000 |
GB9341-2008 |
|
Impact strength Unnotched(KJ/㎡)(23℃±2℃) |
＞45 |
GB1043-1979 |
|
Impact strengrh notch(KJ/㎡)(23℃±2℃) |
＞8 |
|
|
Compressive strength(MPa)(23℃±2℃) |
＞950 |
GB1041-2008 |
|
Tensile strength(MPa)(23℃±2℃) |
＞700 |
GB1040-2006 |
|
Elongation％ |
5.0-7.0 |
GB1040-2006 |
|
Rockwell hardness（HRE） |
80-100 |
GB9342-1988 |
|
Distortion temperature(18.6kg/㎝2)℃ |
≥300 |
GB1634-2004 |
|
Dilatation coefficient（23-200℃），（10﹣5㎝/㎝/℃） |
3.5-5.5 |
GB/T2572-2005 |
|
Friction coefficient（PV=0.33MPa·m/s） |
0.1-0.2 |
GB3960-1983 |
|
Wear volume(cm3) |
(1.0-5.0)×10-5
|
GB3960-1983 |
|
Dielectric constant(1KHz) |
2.0-3.0 |
GB1409-2006 |
|
Surface resistance(Ω) |
1010-1013 |
GB1410-2006 |
|
Volume resistance（Ω·m） |
109-1012 |
GB1410-2006 |
|
Note:When test the sample,you should indicate the model adopted by way of preparation (moulding, extrusion molding) is used in this standard moulding (280-380 ℃) preparation of sample |
||
Product appearance:faint yellow powder.
Product specification:powder,granule,proximate matter
Packing:5kg/bag,25kg/drum